Wire Drawing Powder & Lubricants for Ludhiana & Mandi Gobindgarh Wire Mills
Ludhiana and Mandi Gobindgarh represent the manufacturing powerhouse of North India for bicycle components, fasteners, and secondary steel processing. Operating under high production volumes, mills require lubricants that maintain consistent die box fluidity and die life. Shri Ram Chemicals provides direct factory supply of Calcium wire drawing powders, Sodium lubricants, wet pastes, and drawing oils with express logistics from our Ghaziabad facility to mills across Ludhiana & Mandi Gobindgarh and Punjab.
Moisture-barrier 50 KG HDPE bags on dedicated transport corridors ensuring zero humidity absorption during transit.
Operational Performance Specifications
| Operational Metric | Engineering Specification & Behavioral Range |
|---|---|
| Physical Appearance / Form | Off-White Granular Powder / Charcoal Grey-Black (85 Black) / Amber Liquid / Viscous Paste |
| Lubricant Base Chemistry | Calcium based • Sodium based • Wet Emulsion • Non-Ferrous Oils |
| Maximum Continuous Drawing Speed | Up to 10 m/s (Calcium) • 15 - 20 m/s (Sodium) • 10 - 15 m/s (High Speed Powder) |
| Suitable Substrates | Suitable for Low & Medium Carbon, Binding Wire, Nail Wire, High Carbon & Spring Steel |
| Die Wear Protection | Significantly Extends Die Life |
| Standard Packaging | 50 KG Net Multi-Wall HDPE Moisture-Barrier Bags with Inner Sealed Liner / 200 KG Drums |
| Recommended Storage | Keep Elevated on Pallets in Dry Ambient Warehouse Away from Moisture |
Wire Applications Served Across Ludhiana & Mandi Gobindgarh
check_circle Bicycle Spoke Wire (Medium & High Carbon)
High-tensile drawing across 7 to 9 continuous passes requiring flawless surface finish for subsequent zinc electroplating or bright chrome finish.
check_circle Cold Heading Fastener & Bolt Wire
Wire drawn for fasteners must retain a ductile, protective residual soap film that buffers the cold-upsetting heading punch without flaking or clogging machine grippers.
check_circle High-Carbon Spring Steel & Umbrella Wire
Severe frictional heating in drawing 0.60% to 0.85% C rod demands high-melting sodium and calcium soaps to prevent tensile embrittlement.